陶瓷纤维浇注料产品简介:
Brief
    硅酸铝(陶瓷)耐火纤维浇注料是一种由硅酸铝(陶瓷)耐火纤维经特殊工艺处理后与粒状或粉状耐火材料混合,加入适量的结合剂和水共同组成的,具有较高的流动性,适宜于浇注方式成形的不定形耐火材料。
Silicate Aluminum (ceraminc) re-fractory pouring materials are a kind of unshaped refractory materials are a kind of unshaped refractory materials which are made from silicate aluminum re-fractory fiber disposed by special tech-nology to form granulose and pulverous materials, then adding some binder and water. It is high fluidity and is fit for pouring.产品应用:
Application range
硅酸铝(陶瓷)耐火纤维浇注料通常采用浇注法施工,也可采用喷涂和涂抹法施工,主要应用在工业炉衬或隔热层炉门、观察孔、烧嘴砖、金属熔沟、熔槽等部位。
Silicate aluminum refractory pouring materials are generally used in pouring ways or spurting and daubing ways ,and 硅酸铝纤维浇注料are mainly ap-piled for lining for industry fur-naces or themal insulation door, peep hole, burner tile, metal-melted channel, metal-mdlted trough etc points.

硅酸铝(陶瓷)耐火纤维浇注料
Silicate Aluminum(ceramic)Refractory Pouring Materals

理化指标:(physical properties)

执行GB/T16400-2003标准

 

品名Name

项目
Item

型号Type

标准纤维浇注料material for pouring of standard fiber

高纯纤维浇注料
material for pouring of high-purity fiber

高铝纤维浇注料
material for pouring of high-alumina fiber

含锆纤维浇注料
material for pouring of Zirconia contented

HY-1010
HY-2010
HY-3010
HY-4010

最高使用温度(℃ )
Maximum operating temperature

1000
1100
1300
1400

长期使用温度(℃ )
Concinuous operating
temperature

900
1000
1200
1300

体积密度(t/m3)
Volume density

0.8-0.6
0.8-0.6
1.0-0.6
1.0-0.6

重烧线变化率(﹪)
reheating liner change

2
2
2
2

耐压强度(Mpa)
Compressive resistance

0.6-1.0
0.6-1.0
0.8-1.3
0.8-1.3
AI2O3

≥40

≥45

≥47

≥50

 